On the transition from pushing to engulfment during directional solidification of the particle-reinforced aluminum-based metal-matrix composite 2014+10 vol pct Al2O3

Abstract  Microstructural evolution in the commercial aluminum-based metal matrix composite 2014+10 vol pct Al2O3 was investigated during directional solidification with planar interface within the initial transient. Investigations were